[MW:13014] FW: 13012] RE: 13011] RE: 13008] NACE requirement, does the WPS requirement HIC Test?

By Materials & Welding
 
 
Pradip Goswami,P.Eng.IWE
Welding & Metallurgical Specialist & Consultant
Ontario,Canada.
Email-pgoswami@sympatico.ca,
 

From: pgoswami [mailto:pgoswami@quickclic.net]
Sent: Friday, November 18, 2011 9:25 AM
To: 'sivaselvam@kpoc.com.my'
Subject: RE: 13012] RE: 13011] RE: 13008] NACE requirement, does the WPS requirement HIC Test?

Please look through Annex-A, if this material falls in to the list mentioned no HIC test is required.
 
Thanks.
 
Pradip Goswami,P.Eng.IWE
Welding & Metallurgical Specialist & Consultant
Ontario,Canada.
Email-pgoswami@sympatico.ca,
 

From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] On Behalf Of Sivaselvam Ponandrum
Sent: Friday, November 18, 2011 1:57 AM
To: materials-welding@googlegroups.com
Subject: [MW:13012] RE: 13011] RE: 13008] NACE requirement, does the WPS requirement HIC Test?

Hi,

 

Based on the process requirement, the Pipe is specified for NACE Certification, in addition HIC requirement is specified for pipes/ fitting that fabricated from welded plates, also we specified for HIC is not required for seamless pipe / fittings.

 

 

Now for joining two pipes / fittings together whether it is seamless or welded pipe or fittings (fabricated from plates), does the WPS qualification requires HIC Testing?

 

If yes, what is the HIC Testing Procedure & Acceptance Criteria.?

 

 

Case A

 

 

 

 

Case B

 

 

Case C

 

 

Case F

 

 

 

Case G

 

Case I

 

 

 

Regards

 

Siva

 

Asset Integrity

 

Operation Assurance

From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] On Behalf Of pgoswami
Sent: Friday, November 18, 2011 12:06 PM
To: materials-welding@googlegroups.com
Cc: Sivaselvam Ponandrum
Subject: [MW:13011] RE: 13008] NACE requirement, does the WPS requirement HIC Test?

 

Hello,

 

Your query is too general. Can you specify what're the design requirements, wrt PH2S, PCO2, Temperature or any other design variable.

 

What's the material specification for pipes?

 

Appreciate your response.

 

Thanks.

 

Pradip Goswami,P.Eng.IWE

Welding & Metallurgical Specialist & Consultant

Ontario,Canada.

Email-pgoswami@sympatico.ca,

pgoswami@quickclic.net

 

 

From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] On Behalf Of Sivaselvam Ponandrum
Sent: Thursday, November 17, 2011 3:49 AM
To: materials-welding@googlegroups.com
Subject: [MW:13008] NACE requirement, does the WPS requirement HIC Test?
Importance: High

 

Dear All,

 

For welding carbon steel pipe with NACE requirement, does the WPS qualification requires HIC Test?

 

 

Regards

 

Siva

 

Asset Integrity

 

Operation Assurance

 

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

Comments

Post a Comment

Popular posts from this blog

Re: [MW:34105] SA266 GR4N 4 Cycle SPWHT

By Materials & Welding
Hi,  You are correct, Minimum refers to the one cycle for which this part will expose until final work shop PWHT. hence mill test certificate shall include this.  Max. SPWHT, refers to additional cycles of heat treatment that are reserved for future repairs during equipment lifetime.  Again, these simulated no. Of cycles shall be specified in MTC.  The idea is we need to make sure that steel mechanical properties are not compromised upon exposure to multiple repairs (i e 4 cycles in your case).  One could say, if steel is subjected to 4 cycles and is ok, then it should by defacto be good for one cycle, yet, this is wrong assumption cause mechanical problems and microstructure of materials varies accordingly based on no. Of cycles for which material will expose. This is apparent in alloy steel and especially for impact test values as an example.  In your case, this forged CS with properties before PWHT can be understood to be " as forged" condition (i.e. Wit...
Post a Comment
Read more

Materails FAQs

By Materials & Welding
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...
21 comments
Read more

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

By Materials & Welding
Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change.   Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...
Post a Comment
Read more