We have fabricated a vessel of wall thickness 80mm, Construction code is ASME Section VIII Div.2 Ed. 2010. The vessel is cladded with SS 316L. It also has dissimilar weld joints between nozzle (SS) to Shell (CS) Type Category D, this welding was done using ENiCrFe-3 consumables.
My query is :
As per client he requires PA/UT to be done on the category D joints. But as per our NDT subcontractor PA/UT cannot be done for inconel welds, the rays will not penetrate through the welds. Hence requesting you to suggest a suitable method for carrying out the NDT of the same. Is there any technique/Method where we can propose to client, so that NDT can be completed.
Yours views on the same will higly appreciated,
Regards,
Josenit
-- To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
No comments:
Post a Comment