[MW:23286] RE: 23284] UT or PAUT lieu of RT for Pipes, Tubes in Boiler/ Power Piping.

Mr. Sudalai,

Please find the following attached articles for your information.The relevant ASME code cases are also mentioned.Many of these code cases are annulled to the main design code. However if you search in IHS or in the web you may find each code section specific code case.

PAUT would require more detailed training and interpretation skills for the operators, which may be a hindrance.

Thanks.

Pradip Goswami, P.Eng,IWE

Welding & Metallurgical Engineer/Specialist

Ontario, Canada

pgoswami@quickclic.net

pradip.goswami@gmail.com

From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] On Behalf Of Sudalai Kannan
Sent: Thursday, May 14, 2015 10:00 AM
To: materials-welding@googlegroups.com
Subject: [MW:23284] UT or PAUT lieu of RT for Pipes, Tubes in Boiler/ Power Piping.

Dear Experts,

Can you please give the reference below?

We have 2000 butt weld joints (2” * 6mm Thick) for RT in Power Boiler and the project time is so short and we proposed PAUT lieu of RT to our client.

Then client ask the reference from the code and we referred PW-11 & 52 as per ASME Sec. I but PW-11 is clearly mentioned that UT shall be carried out in circumferential weld of pipes and tubes more than 4” or thickness more than 13mm.

Can you please give the reference from ASME section to UT or PAUT lieu of RT for 6mm thickness of Pipe or Tube or power pipe.

Thanks & best regards,

M.Sudalai,

QA/QC Engineer.

--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at http://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CA%2BZM_eaZ_yLQt--N4vz7OOOGS01ZzzS0G0QMWVL39btN-X3-Dg%40mail.gmail.com.
For more options, visit https://groups.google.com/d/optout.

No virus found in this message.
Checked by AVG - www.avg.com
Version: 2015.0.5941 / Virus Database: 4342/9775 - Release Date: 05/14/15

Materails FAQs

Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...

[MW:30043] Weep hole

If weep hole is not provided in dummy pipe before welding What will happen??? -- https://materials-welding.blogspot.com/ https://www.linkedin.com/groups/122787 --- You received this message because you are subscribed to the Google Groups "Materials & Welding" group. To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com . To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/da251ee6-fa7f-4851-b876-cdb3834ae341%40googlegroups.com .

[MW:36169] Cold Bending Qualification

Dear Experts, Can anyone share the inspection requirements or a qualification procedure for cold bending? Our client spec states only the requirements for induction bending and would like to know your opinion on the cold bend inspection requirements. The code of construction is B31.3, Max. 5D bends, A106 SS 316L. Thanks in Advance. -- https://materials-welding.blogspot.com/ https://www.linkedin.com/groups/122787 --- You received this message because you are subscribed to the Google Groups "Materials & Welding" group. To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com . To view this discussion visit https://groups.google.com/d/msgid/materials-welding/1be61cc3-e9c9-4a5f-834d-e8485e248432n%40googlegroups.com .

Materials & Welding

Search This Blog