Dear All,
-- Code : ASME Sec VIII Div.1
Shell Material : SA 516 Gr.60
Nozzle Material : UNS N06625
UCS 56 (c) When pressure parts of two different P‐Number groups are joined by welding, the postweld heat treatment shall be that specified in either of Tables UCS-56-1 through UCS-56-11 or Tables UHA-32-1 through UHA-32-6, with applicable notes, for the material requiring the higher postweld temperature.
My question is regarding the PWHT requirements for above vessels,
1.Does the shell to nozzle weld edges to be buttered by Er NiCrMo-3 before PWHT and groove welding by Er NiCrMo-3 after PWHT?
or
2.Or a PQR of dissimilar joint P1 to P43 with PWHT (of P1 requirements) can be used directly?
UNF 56 : Does not address such dissimilar joint
UNF-56 POSTWELD HEAT TREATMENT
(a) Postweld heat treatment of nonferrous materials is not normally necessary nor desirable.
Kindly share your experience/recommendations.
Thanks.
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at http://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/e36217a3-478d-4762-84ea-8a6430a05a99%40googlegroups.com.
For more options, visit https://groups.google.com/d/optout.
No comments:
Post a Comment