[MW:23038] RE: 23031] Local PWHT of butt welds in piping

The following link may be of use to you.

http://www.twi-global.com/technical-knowledge/job-knowledge/heat-treatment-of-welded-joints-part-3-116/

 

The other articles by TWI under the same topic should also be of interest.

 

Best wishes

 

Alan Denney

 

From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] On Behalf Of Vishwas Keskar Welding Manager Pune India
Sent: 25 May 2015 16:29
To: materials-welding@googlegroups.com
Subject: [MW:23031] Local PWHT of butt welds in piping

 

For long piping(Carbon steel, alloy steel), butt welding of large diameter(219mm OD TO 606mm OD, THK - 18.26mm to 42 mm )pipes is carried out. 

For PWHT of these butt welds, what are the parameters shall be considered for effective PWHT?

--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at http://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/123817e2-66c9-440c-9da6-21d6b616ce26%40googlegroups.com.
For more options, visit https://groups.google.com/d/optout.

No comments:

Re: [MW:35289] Welding consumable for S355J2WP material

S355 J2 WP  is a weathering structural steel  It has better atmospheric corrosion resistance. Use E 8018 - W1/W2  Electrodes This is regular...