Monday, May 11, 2015

Re: V/v: [MW:23266] Cracking on bending test

So, if this filler metal was used correctly there would be no hot cracks there.
Please try to measure hardness in the area of cracks and compare with those of base metals

best regards

Dr. Georgios Dilintas

Authorized Nuclear Inspector
Authorized Inspector Supervisor

I&F REGIONAL TECHNICAL MANAGER
BUREAU VERITAS PIRAEUS - GREECE

Tel: +30 210 40 63 113 /4 /5
Fax: +30 210 40 63 118
Cell: +30 69 44 64 62 04


tuanpvecc---10/05/2015 06:50:17---‎We used e309t1-1 Gửi từ điện thoại thông minh BlackBerry 10. Từ:  george.dilintas@gr.bureauveritas.

From: tuanpvecc@gmail.com
To: "george.dilintas@gr.bureauveritas.com" <materials-welding@googlegroups.com>, nguyen tuan <materials-welding@googlegroups.com>
Date: 10/05/2015 06:50
Subject: V/v: [MW:23258] Cracking on bending test
Sent by: materials-welding@googlegroups.com





‎We used e309t1-1

Gửi từ điện thoại thông minh BlackBerry 10.
    Từ: george.dilintas@gr.bureauveritas.com
    Đã gửi: 0:57 Chủ nhật, ngày 10 tháng năm năm 2015
    Đến: nguyen tuan
    Trả lời đến: materials-welding@googlegroups.com
    Chủ đề: Re: [MW:23247] Cracking on bending test

What type of filler metal did you use

Sent from my BlackBerry 10 smartphone.
    From: nguyen tuan
    Sent: Σάββατο, 9 Μαΐου 2015 - 07:23
    To: materials-welding@googlegroups.com
    Reply To: materials-welding@googlegroups.com
    Subject: [MW:23236] Cracking on bending test

Hi All

We have bending test for PQ (welding process FCAW , Material CS to stainless steel ) result was fail (cracked). But We check PT can't find cracking .
Do somebody have same problem . what is conclusion .

Thanks you

Tuan

--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to
materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to
materials-welding@googlegroups.com.
Visit this group at
http://groups.google.com/group/materials-welding.
To view this discussion on the web visit
https://groups.google.com/d/msgid/materials-welding/a35ad4f0-c336-479f-bfff-6d0f63a8100d%40googlegroups.com.
For more options, visit
https://groups.google.com/d/optout.

This message contains confidential information. To know more, please click on the following link: http://disclaimer.bureauveritas.com 

--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to
materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to
materials-welding@googlegroups.com.
Visit this group at
http://groups.google.com/group/materials-welding.
To view this discussion on the web visit
https://groups.google.com/d/msgid/materials-welding/20150509175733.6443092.17956.5787%40gr.bureauveritas.com.
For more options, visit
https://groups.google.com/d/optout.

--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to
materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to
materials-welding@googlegroups.com.
Visit this group at
http://groups.google.com/group/materials-welding.
To view this discussion on the web visit
https://groups.google.com/d/msgid/materials-welding/20150510034012.4399182.72837.4428%40gmail.com.
For more options, visit
https://groups.google.com/d/optout.

This message contains confidential information. To know more, please click on the following link: http://disclaimer.bureauveritas.com

No comments:

Re: [MW:35289] Welding consumable for S355J2WP material

S355 J2 WP  is a weathering structural steel  It has better atmospheric corrosion resistance. Use E 8018 - W1/W2  Electrodes This is regular...