My question is regarding the PWHT requirements for above vessels,
1.Does the shell to nozzle weld edges to be buttered by Er NiCrMo-3 before PWHT and groove welding by Er NiCrMo-3 after PWHT?
YES.
or
2.Or a PQR of dissimilar joint P1 to P43 with PWHT (of P1 requirements) can be used directly?
P43PWHT NOT RECCOMENDED.HENCE GO WITH OPTION ABOVE.
UNF 56 : Does not address such dissimilar joint
UNF-56 POSTWELD HEAT TREATMENT
(a) Postweld heat treatment of nonferrous materials is not normally necessary nor desirable.
Kindly share your experience/recommendations.
Thanks.
--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at http://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/d58d30c9-1ac9-4f9d-a964-5905542615b4%40googlegroups.com.
For more options, visit https://groups.google.com/d/optout.
Subscribe to:
Post Comments (Atom)
Re: [MW:35289] Welding consumable for S355J2WP material
S355 J2 WP is a weathering structural steel It has better atmospheric corrosion resistance. Use E 8018 - W1/W2 Electrodes This is regular...
-
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? ...
-
Definition of buttering from ASME Section IX, QW/QB-492 Definitions: Buttering: the addition of material, by welding, on one or bot...
-
Section I. PRINT READING 3-1. GENERAL a. Drawings . Drawing or sketching is a universal language used to convey all necessary information to...
No comments:
Post a Comment