[MW:27210] Reduction of wall thickness of dishends after forming.

Hello friends,

we are fabricating dishends with 70 mm thick and 1371 mm I.D .And we hot form the blank the thickness of the final product its thickness is reduces to 3.2 mm after forming and after rectification it becomes 62mm thick and we want more than 63mm what we will do, can anyone suggest me.


Thanks & Regards,
Punit pandey.
Email-punit13pandey@gmail.com

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.

No comments:

Re: [MW:35289] Welding consumable for S355J2WP material

S355 J2 WP  is a weathering structural steel  It has better atmospheric corrosion resistance. Use E 8018 - W1/W2  Electrodes This is regular...