Dear Experts
I need query on Aluminium welding
Material -6061-T6
Material Thickness-16mm
Filler wire- ER4046
Process-GMAW
Pre heat-70 centigrade
Interpass- 120 centigrade
Preclean by Acetone cleaner and SS wire brush
Gas-Ulta high purity Argon gas
During PQR qualifications we face failure in bend test. Crack open at 30degree itself. Is the above method required PWHT after welding. If so what is the method of PWHT and cycle.
Kindly clarify?
Thanks in advance
Regards
Sathish
--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.
Subscribe to:
Post Comments (Atom)
Re: [MW:35289] Welding consumable for S355J2WP material
S355 J2 WP is a weathering structural steel It has better atmospheric corrosion resistance. Use E 8018 - W1/W2 Electrodes This is regular...
-
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? ...
-
Definition of buttering from ASME Section IX, QW/QB-492 Definitions: Buttering: the addition of material, by welding, on one or bot...
-
Section I. PRINT READING 3-1. GENERAL a. Drawings . Drawing or sketching is a universal language used to convey all necessary information to...
No comments:
Post a Comment