[MW:27175] RE: 27172] X65 to X52

Dorh,

 

Please see the relevant extracts from API-1104 as below. According to the rationale below, a change of base metal is essential variable.

 

The  variables(welding consumables, preheat, inter pass control …… & others )  for  welding  X-65- X65  steel   should be followed , for welding X65 to X52 pipe. However a separate  procedure qualification test  is required.

 

I would say this point should be clarified with the AI  or the client to obtain any concession if any???

 

Thanks.

 

P.Goswami.P.Eng, IWE.

Welding & Metallurgical Specialist

Linkedin: https://www.linkedin.com/in/pradip-goswami-2999855/

Email:pgoswami@quickclic.net,pradip.goswami@gmail.com

 

 

5.3.2.2 Materials

The materials to which the procedure applies shall be identified. API 5L pipe, as well as materials that conform to other product specifications, may be grouped (see 5.4.2.2), provided that the qualification test is made on the material with the highest specified minimum yield strength (SMYS) in the group.

 

5.4.2.2 Base Material

A change in base material constitutes an essential variable. When welding materials of two separate material groups, the procedure for the higher strength group shall be used. For the purposes of this standard, all materials shall be grouped as follows.

a)     SMYS less than or equal to that of the material specified as API 5L Grade X42;

b)    b) SMYS greater than that of the material specified as API 5L Grade X42 but less than that of the material specified as API 5L Grade X65;

c) for materials with a SMYS greater than or equal to that of the material specified as API 5L Grade X65, each grade shall receive a separate qualification test.

 

 

From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] On Behalf Of dorh
Sent: December 12, 2017 11:29 AM
To: Materials & Welding <materials-welding@googlegroups.com>
Subject: [MW:27172] X65 to X52

 

dear friends,

 

I have a PQR for X65 to X65 pipe, can I formulate a WPS for welding X65 to X52 pipe

BR

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.


Virus-free. www.avg.com

1 comment:

Anonymous said...

If I weld x65 to x65 with 7010-A1 root pass and 7010 fill and cap, will I meet the tensile and yield to meet X65 with out preheat and try and maintain a low inter-pass temp

Re: [MW:35289] Welding consumable for S355J2WP material

S355 J2 WP  is a weathering structural steel  It has better atmospheric corrosion resistance. Use E 8018 - W1/W2  Electrodes This is regular...