RE: [MW:11525] SA82 F316L Flanges

No you cannot accept without Solution annealing refer below content taken from ASME Section 2 A.

5. Heat Treatment

5.1 After hot working, forgings shall be cooled to a

temperature below 1000°F [538°C] prior to heat treating

in accordance with the requirements of Table 1.

5.2 Low Alloy Steels and Ferritic and Martensitic

Stainless Steels — The low alloy steels and ferritic and

martensitic stainless steels shall be heat treated in accordance

with the requirements of 5.1 and Table 1.

 

With kind regards,

Vinod Kumar Kataria

GM - Operations

Bliss Anand Private Limited,

92B/93B Sector 5

IMT Manesar,Gurgaon,

National Capital Region Delhi.

India .

Phone : +91-124-4366000 (9 Lines)

Mobile Phone : +91-9560199004

Fax : +91-124-2290884

 

From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] On Behalf Of narayanasamy kumar
Sent: Wednesday, June 29, 2011 7:57 PM
To: materials-welding@googlegroups.com
Subject: Re: [MW:11517] SA82 F316L Flanges

 

Dear Experts,

           

            Can anybody tell SA 182 F316L 1" Flanges we received without Solution annealing, Is it acceptable? Please let me know code reference.(ASME SEC II A).

 

Thanks and Regards,

Kumar.

Singapore.

 

---

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.