Re: [MW:11498] Re: Welding in Poland

Mr.Raja,
Can you tel me why DNV cannot witness test and Approve PQR n WPQ as per ASME?
Muni

On Fri, Jun 24, 2011 at 1:29 PM, graja <agrajewski@gmail.com> wrote:

Hi,

as I know UDT and DNV Poland don't have ASME authorized inspector to
approve or coordinate welding acc. ASME, but TUV NORD, TUV Rheinland
or Lloyd Register in Poland have ASME authorized inspector so you can
ask them about ASME subject.

I work a little beat with ASME and if you don't have special
requirements about 3rd part you can approved PQR and WPQ by yourself.

sorry for my English, I have hope I help.

On Jun 23, 4:17 am, <vinit.deshpa...@akersolutions.com> wrote:
> Dear Experts,
>
> Need you your Help.
>
> One of our supplier has informed us that ''We cannot perform welding according to ASME because DNV Poland don't have accreditation for ASME''.
>
> As per my knowledge UDT is-Office of Technical Inspection working as an Inspection Body, as the Notified Body and the Recognized Third Party Organization as the Certification Body.
>
> Hence its a Inspection body only, my questions are as below,
>
> Is my understanding about UDT is correct?
>
> Can we do welding as per ASME in Poland?
>
> What are the options to be considered If we need to do welding in Poland according to ASME.
>
> Your early reply in this regard is appreciated
>
> Regards,
> Vinit Deshpande
> Aker Solutions
> Tel: +47-67826358
> Mobile: +47-45217814

> Email: Vinit.Deshpa...@akersolutions.com

>
> -
> This e-mail and any attachment are confidential and may be privileged or otherwise protected from disclosure. It is solely intended for the person(s) named above. If you are not the intended recipient, any reading, use, disclosure, copying or distribution of all or parts of this e-mail or associated attachments is strictly prohibited. If you are not an intended recipient, please notify the sender immediately by replying to this message or by telephone and delete this email and any attachments permanently from your system.

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

Re: [MW:34105] SA266 GR4N 4 Cycle SPWHT

Hi, You are correct, Minimum refers to the one cycle for which this part will expose until final work shop PWHT. hence mill test certificate shall include this. Max. SPWHT, refers to additional cycles of heat treatment that are reserved for future repairs during equipment lifetime. Again, these simulated no. Of cycles shall be specified in MTC. The idea is we need to make sure that steel mechanical properties are not compromised upon exposure to multiple repairs (i e 4 cycles in your case). One could say, if steel is subjected to 4 cycles and is ok, then it should by defacto be good for one cycle, yet, this is wrong assumption cause mechanical problems and microstructure of materials varies accordingly based on no. Of cycles for which material will expose. This is apparent in alloy steel and especially for impact test values as an example. In your case, this forged CS with properties before PWHT can be understood to be " as forged" condition (i.e. Wit...

Materails FAQs

Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change. Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...

Materials & Welding

Search This Blog