I have faced regarding hardness issue on ASTM A 335 GR P-11 material.
Pipe thickness is 7.5mm. Without PWHT hardness is coming around 275
to 289 BHN on weld zone & 250 260 BHN on HAZ zone & parent material
hardness is 197 to 204 BHN. Due to inside refractory material PWHT is
not possible.
My question is as per ASME B-31.3/ ASME SEC II PART A hardness value
of this material is 225 BHN ( MAX). There is any specification for
weld zone / HAZ zone hardness value.
Can anybody give an idea to reduce the hardness without PWHT if it is
not acceptable limit.
Thanx in advance.
Regards
Pradip
--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
No comments:
Post a Comment