We also faced this kind of situation where we have overwhelmed through the dress inside the root. These kind of undercuts would act as a stress point during service and invite fatigue crack, however it depends up on the nature of service where pressure, temperature and cyclic load matters.
I would suggest you to make it level by dressing inside if possible. Or else, decision should be taken combinely by your all concerned.
Thanks,
On 22 Mar 2019 3:58 am, "Muhammed Ibrahim PK" <ibratech@gmail.com> wrote:
Gents,I am getting the attached image in boroscope inspection at root. But RT not showing any density variation or undercut. Please give your comment on it.--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.
No comments:
Post a Comment