Hi,
ER 430 is correct consumable, but you need PWHT.
With out PWHT I have qualified with E NiCrMO3.
E 309L will not pass in bend test.
Regards
NV. PRASAD
+ 968 95332803
On 7/31/15, pradip kumar Sil <pradipsil@gmail.com> wrote:
> Dear All,
>
> We have to weld A-240 TP 409 to A-240 TP 409 ( P-7 to P-7 Material ) &
> which Filler we can use ER 309L /ERNiCr-3.
> Temperature is around 300 degree centigrade ( HRSG Bottom area this
> material is coming ) where this wps will be used.
> Thanks in advance
> Regards
> Pradip
>
> --
> You received this message because you are subscribed to the Google Groups
> "Materials & Welding" group.
> To unsubscribe from this group and stop receiving emails from it, send an
> email to materials-welding+unsubscribe@googlegroups.com.
> To post to this group, send email to materials-welding@googlegroups.com.
> Visit this group at http://groups.google.com/group/materials-welding.
> To view this discussion on the web visit
> https://groups.google.com/d/msgid/materials-welding/CAB%3DAs8kd5BZtnMBjaza5GytD9s5VfyD%2BqLzXATNZQi6DGEZSKw%40mail.gmail.com.
> For more options, visit https://groups.google.com/d/optout.
>
--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at http://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAL%3D4YYiutvm4%2BkV%2BBWGH-o2CqFb0Rnn%2BUFyU-prYHruGg%2BhOnQ%40mail.gmail.com.
For more options, visit https://groups.google.com/d/optout.
ER 430 is correct consumable, but you need PWHT.
With out PWHT I have qualified with E NiCrMO3.
E 309L will not pass in bend test.
Regards
NV. PRASAD
+ 968 95332803
On 7/31/15, pradip kumar Sil <pradipsil@gmail.com> wrote:
> Dear All,
>
> We have to weld A-240 TP 409 to A-240 TP 409 ( P-7 to P-7 Material ) &
> which Filler we can use ER 309L /ERNiCr-3.
> Temperature is around 300 degree centigrade ( HRSG Bottom area this
> material is coming ) where this wps will be used.
> Thanks in advance
> Regards
> Pradip
>
> --
> You received this message because you are subscribed to the Google Groups
> "Materials & Welding" group.
> To unsubscribe from this group and stop receiving emails from it, send an
> email to materials-welding+unsubscribe@googlegroups.com.
> To post to this group, send email to materials-welding@googlegroups.com.
> Visit this group at http://groups.google.com/group/materials-welding.
> To view this discussion on the web visit
> https://groups.google.com/d/msgid/materials-welding/CAB%3DAs8kd5BZtnMBjaza5GytD9s5VfyD%2BqLzXATNZQi6DGEZSKw%40mail.gmail.com.
> For more options, visit https://groups.google.com/d/optout.
>
--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at http://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAL%3D4YYiutvm4%2BkV%2BBWGH-o2CqFb0Rnn%2BUFyU-prYHruGg%2BhOnQ%40mail.gmail.com.
For more options, visit https://groups.google.com/d/optout.
Comments