Re: [MW:23288] cracke- Moc ss cap thk-2.5 mm

weld sequence mean ? pl. describe 

On Saturday, 8 August 2015 14:54:07 UTC+5:30, Shanmuga sundaram wrote:

May be weld sequence is wrong please go to IACS No: 47

Sent from my iPhone

On 07-Aug-2015, at 8:17 pm, Kunal Patel <kunal.pa...@gmail.com> wrote:

dear expert,

pl. review the attached photo first. let me know, what are the causes for crack developed in weld joints between cap to condenser flange ?
I observed crack at fillet weld joints (partition plate to cap inside surface) - how it was occurred ? would both cracks be intersected from inside ?

your valuable reply will be appreciable.

r/s
Kunal Patel
Bureauveritas

 

--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com.
To post to this group, send email to material...@googlegroups.com.
Visit this group at http://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/09227af6-f6b2-4a81-a4a4-df1105600d40%40googlegroups.com.
For more options, visit https://groups.google.com/d/optout.

<IMG-20150807-WA0010.jpg>

<IMG-20150807-WA0011.jpg>

<IMG20150807165540.jpg>

<IMG20150807165613.jpg>

--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at http://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/0ea064f0-3082-4987-ba1e-fd1539644d99%40googlegroups.com.
For more options, visit https://groups.google.com/d/optout.