Re: [MW:19314] IGC practice E test undertanding

Acceptance is no grain dropping and cracks not carbide precepitation
Also structure is not ditch than it is acceptable as per a 262

On Nov 13, 2013 5:13 PM, "krishna mudhale" <kmudhale@gmail.com> wrote:
Dear experts,
As per technical specification of customer says that IGC practice E
for stainless steel SS 316L material shall be carried out and that
bend test specimen shall be examined at a magnification of 200X and
bent specimen shall be free of any cracks or grain dropping.
And we performed this test on coupon and at 20X appearance of fissures
or cracks not observed and IGC E is accepted as per lab report, But at
200X magnification intergranular attack(heavy carbide precepitation)
observed near outer radius of bent specimen and our client is not
accepting this carbide precepation.
So pleare share your views and is it acceptable or not.
--
With Warm Regards
Krishna Mudhale

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm

The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
For more options, visit https://groups.google.com/groups/opt_out.

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
 
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
For more options, visit https://groups.google.com/groups/opt_out.

No comments:

[MW:35346] Cast-iron welding

Any advice for cast iron welding Sent from Yahoo Mail for iPhone