you can weld two dissimilar thick pipes and fittings by making proper transition of higher thickness to lower thickness.
Transition slope should be 1:3. Please refer figure UW-13.1 of ASME VIII DIV 1 for better understanding.
Best regards
Atul Khatri
On Fri, Apr 17, 2020 at 9:00 AM Dinesh Somwanshi <som.din@gmail.com> wrote:
It's shall not lowered down to design thicknesses.You may do smooth tempering to match if above meets.Dinesh--On Thu, Apr 16, 2020, 19:31 QA/QC <adnanziad49@gmail.com> wrote:Hello everyone--im asking for any information about the maximal thickness to weld between two different wall thickness from B31.3 or b.16.25in my case we want to weld 12'' THICKNESS 25.4 WITH 12.7 ITS POSSIBLE RE-SCHDULING THE INTERNAL THICKNESS FOR 12MM OR THER IS A MAXIMUM THICKNESS LIMITSBEST REGARDS
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/f4e88916-9f58-4f94-8cad-5d6e69c079dc%40googlegroups.com.
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAELgRrUzizugTBeWVtZcxmhSiAwD5qw8HiiZ6mrMAJ5nDNps6A%40mail.gmail.com.
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CACKOSeAC8Xky8NobPeC7ShVdqwO--DzMVgm_GnoQQ8ABMX-cLw%40mail.gmail.com.
No comments:
Post a Comment