Re: [MW:30727] BASE METAL THIKNESS FOR PQR

Instead of being confused, first you should know what is your Job.

Then the design  Code ASME B 31.4 or ASME B31.8

Snap shot provided below for you to decide.

See below requirement and snap shot of ASME B 31.8

Thanks & Regards

J.Gerald Jayakumar

On Thursday, April 9, 2020, 05:00:52 PM GMT+7, QA/QC <adnanziad49@gmail.com> wrote:

IM CONFUSED , NORMALLY WHAT I SHOULD TO USE ASME 9 OR API 1104  

Le jeudi 9 avril 2020 07:02:56 UTC+2, gerr...@yahoo.com a écrit :

By below mail was based on API 1104 Code which considers yield strength as essential variable.

From your below mail I understand you are using ASME Sec.IX (correct me of I am wrong).

Acc to ASME Sec.IX one PQR is sufficient for API 5L X60 - X65 as they both fall under P1 Gr.2.

Acc to ASME Sec.IX thickness range qualified is 1.5mm to 15.84mm

Thanks & Regards

J.Gerald Jayakumar

On Thursday, April 9, 2020, 11:23:55 AM GMT+7, QA/QC <adnan...@gmail.com> wrote:

tnx for your reply 

So its mean that i should prepare two different Test coupon or what 

and for the maximum thikness of base metal from QW 451.1 THEY MENTION THAT  T QUALIFIED X 2  ITS MEAN 7.92 X2 = 15.84 mm

Le mercredi 8 avril 2020 13:52:38 UTC+2, gerr...@yahoo.com a écrit :

Considering Pipeline, API 1104 code was considered for below.

1. One PQR for X60 material

2. Another PQR for X65 material to be qualified'

If you qualify PQR on 6 inch wall thickness 7.92 mm then it qualifies from wall thickness 4.8mm to 19.1mm and no Limitation on Diameter

Thanks & Regards

J.Gerald Jayakumar

On Wednesday, April 8, 2020, 03:10:03 PM GMT+7, QA/QC <adnan...@gmail.com> wrote:

Hello 

i want to prepare a WPS for pipeline work with base metal API 5L X60 - X65  SMAW 

for the test coupon i want to use 6" with thickness = 7.92 mm 

want to know the minimum and maximum range for size and thickness used for the PQR 

BEST REGARDS

--
https://materials-welding. blogspot.com/
https://www.linkedin.com/ groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to material...@ googlegroups.com.

To view this discussion on the web visit https://groups.google.com/d/ msgid/materials-welding/ 0230b3b5-7871-4efa-94d7- 609f4effa70a%40googlegroups. com.

--
https://materials-welding. blogspot.com/
https://www.linkedin.com/ groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to material...@ googlegroups.com.
To view this discussion on the web visit

https://groups.google.com/d/ msgid/materials-welding/ 94cc40bc-2a64-4a7c-828d- 034cc090d77b%40googlegroups. com

.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit

https://groups.google.com/d/msgid/materials-welding/acc75da4-18b3-44c6-9398-91d01641143b%40googlegroups.com

.