Dear ,,--1) As per the Weld Joint Preparation is "Single Bevel" But after welding it seen like "Single Vee" with other side bevel of 10° – What Joint configuration will be Considered in the PQR / WPS as Result -- Single V
2) The attached Macro Photograph is seen that Root is not Penetrated with Backing Plate. – is this Result shall be Passed or failed. First thing i understand you looking for full penetration joint by putting backing plate.second thing how could be possible to obtain full penetration near narrow edge of root with small opening, As gas cup size some about 15 mm in diameter ? It cause ARC improper fray at root pass location. You must maintain ROOT gap IF looking for it. With Micros it looks like faying surface has better control over hot , fill , cap .Thanks & RegardsDINESH VITTHAL SOMWANSHI
BACHELOR IN MECHANICAL ENGINEER
Skype = dinesh somwanshi
असो द्यावी दया तुमच्या लागतसे पाया.
*Pray for others, sometime, You might never need to pray for yourself
again.....*On Thu, Nov 30, 2017 at 1:39 PM, Mayur Hiremath <hiremath.qaqc@gmail.com> wrote:--Dear All,Good Morning,Please refer the attached Macro Photograph extracted from the single PQR test Coupon & Joint Preparation details. The thickness of test Coupon is 30 mm Grade of Material S460 ML & backing plate with 10 MM same Grade. The Weld Process is FCAW. PQR qualification is according to AWS D1.1 2015.
Based on the attached please clarify the Below comments is the Result to be Passed or Reject.
1) As per the Weld Joint Preparation is "Single Bevel" But after welding it seen like "Single Vee" with other side bevel of 10° – What Joint configuration will be Considered in the PQR / WPS as Result
2) The attached Macro Photograph is seen that Root is not Penetrated with Backing Plate. – is this Result shall be Passed or failed.
Waiting for your valuable Response / comments with explanation stating Passed or Failed.Regards,HIREMATH
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com .
Visit this group at https://groups.google.com/group/materials-welding .
For more options, visit https://groups.google.com/d/optout .
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.
Thursday, November 30, 2017
Re: [MW:27087] Macro Photograph of PQR & Joint Preparation
Dear Dinesh,
Thanks for Quick Reply appreciated .
Sir,
The Root Gap is 4mm we are welding it FCAW process Size is 1.2, it can be fusion with backing plate.
However As per the AWS 4.9.1.1 (3)the weld shall be complete fusion (fig 5.4) . If we refer Macro photograph it is not fused with backing plate also it is in concave fusion. Can be passed or reject the PQR.
Regards,
HIREMATH
Subscribe to:
Post Comments (Atom)
Re: [MW:35289] Welding consumable for S355J2WP material
S355 J2 WP is a weathering structural steel It has better atmospheric corrosion resistance. Use E 8018 - W1/W2 Electrodes This is regular...
-
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? ...
-
Definition of buttering from ASME Section IX, QW/QB-492 Definitions: Buttering: the addition of material, by welding, on one or bot...
-