But question is that when the repair area has to be repaired either
area exceeds 58cm2 or less.
On 7/23/12, Vinayak Kale <Vinayak_Kale@lntenc.com> wrote:
> It means , unbounded area to be removed & repair , recently i have face the
> same problem in cladded dish end , we removed complete cladded area by
> machining & rewelded with SAW process
>
> Regards
>
>
> Vinayak Kale
> OGSP - QA & I , HC - Upstream
> EPC Block , 2nd Floor , Gate No.1
> Saki Vihar Rd. Powai Campus
> Mumbai - 400072
> Ph : + 91 022 6705 3969
> (M) - 9987875309
> www.larsen toubro.com
>
>
> -----materials-welding@googlegroups.com wrote: -----
>>
>> To: materials-welding@googlegroups.com
>> From: kundan.ahirao@gmail.com
>> Sent by: materials-welding@googlegroups.com
>> Date: 07/23/2012 12:23PM
>> Subject: [MW:14925] Repair of cladding plate as per SA 264
>>
>> Dear Expert
>> please advice-----
>> Recently we received some explosion bonded clad plate of SA516 gr 70 + SA
>> 240 Tp 316L.
>> During explosion bonding plate having unbonded area.
>> As per SA 264 cl No 13.3.3 says that no single unbonded area exceeding
>> 58cm2 with total unbonded area not to exceed 5% of the total cladded
>> surface area.
>> Does it mean that above 58cm2 unbonded area are not acceptable or above
>> 58cm2 unbonded area repairable upto 5% of total cladded surface area.
>>
>> Thanks and Regards
>>
>> --
>> To post to this group, send email to materials-welding@googlegroups.com
>> To unsubscribe from this group, send email to
>> materials-welding+unsubscribe@googlegroups.com
>> For more options, visit this group's bolg at
>> http://materials-welding.blogspot.com/
>> The views expressed/exchnaged in this group are members personel views and
>> meant for educational purposes only, Users must take their own decisions
>> w.r.t. applicable code/standard/contract documents.
>
> --
> To post to this group, send email to materials-welding@googlegroups.com
> To unsubscribe from this group, send email to
> materials-welding+unsubscribe@googlegroups.com
> For more options, visit this group's bolg at
> http://materials-welding.blogspot.com/
> The views expressed/exchnaged in this group are members personel views and
> meant for educational purposes only, Users must take their own decisions
> w.r.t. applicable code/standard/contract documents.
>
--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
Subscribe to:
Post Comments (Atom)
[MW:34866] Presentation for WPS ,PQR AND WPQ as per ASME Sec IX in power point
Dear Experts. If anyone having presentation of WPS,PQR and WPQ as per ASME SEC.IX in power point then please share . Regards Sanja...
-
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? ...
-
Definition of buttering from ASME Section IX, QW/QB-492 Definitions: Buttering: the addition of material, by welding, on one or bot...
-
Section I. PRINT READING 3-1. GENERAL a. Drawings . Drawing or sketching is a universal language used to convey all necessary information to...
No comments:
Post a Comment