Dear expert
kindly advice and share your opinion
we have cladding of SA516 gr 70 + SA 240 tp 410S.
After explosion bonding manufacturer is giving SR cycle to clad plate at soaking temp 675 deg C.
But at this temperature tensile strength of base metal will achieve or not.
If not then what will be soaking temperature.
Also as per our fabrication drg soaking temp given is 620 deg C.
Thanks and regards
--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
Subscribe to:
Post Comments (Atom)
-
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? ...
-
Definition of buttering from ASME Section IX, QW/QB-492 Definitions: Buttering: the addition of material, by welding, on one or bot...
-
Section I. PRINT READING 3-1. GENERAL a. Drawings . Drawing or sketching is a universal language used to convey all necessary information to...
No comments:
Post a Comment