Re: [MW:8380] Hydrotesting Pressure gauge calibration

By Materials & Welding
Best practice is get to calibrated before every test but keeping in mind the commercial aspects a six month time period or client specs can be followed. it  also depends on how many times you are using the gauge in the stipulated time period.
 
Best regards
Sohale

From: Sundaram Elumalai <Elumalai.Sundaram@starfab.com.sa>
To: materials-welding@googlegroups.com
Sent: Thu, November 25, 2010 12:57:24 PM
Subject: RE: [MW:8375] Hydrotesting Pressure gauge calibration

Some Client – ARAMCO requires every 30 days. Please check your client spec also.

 

With Kind regards,

S.Elumalai.

From: materials-welding@googlegroups.com [mailto: materials-welding@googlegroups.com ] On Behalf Of Karthik
Sent: Thursday, November 25, 2010 10:13 AM
To: materials-welding@googlegroups.com
Subject: Re: [MW:8373] Hydrotesting Pressure gauge calibration

 

Hi,
Pressure gauge calibration time shall be in every 6 months as per the normal practice and various project specifications.

Thanks & Regards,

 

(Karthik)

 

Karthikeyan.S

QA/QC Manager

Getabec Energy Co.,Ltd.

379,Moo6,Soi8,Nikhomphatana,

Rayong-21180,

Thailand.

Phone: 0066 38 897035-8 (Off)

Fax: 0066 38 897034

Hand Phone: 0066 892512282



--- On Thu, 11/25/10, Praveen Kumar <praveenkumar.sek@gmail.com> wrote:


From: Praveen Kumar <praveenkumar.sek@gmail.com>
Subject: [MW:8372] Hydrotesting Pressure gauge calibration
To: materials-welding@googlegroups.com
Date: Thursday, November 25, 2010, 1:22 PM

Dear All,

 

Can you pls Suggest as the Piping Hydrotesting Pressure gauge calibration period of time,

and also is there any code/stds governing for this.

 

 

 

Regards,

 

Praveen Kumar

Mechanical Engineer

 

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

 

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

Comments

Post a Comment

Popular posts from this blog

Materails FAQs

By Materials & Welding
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...
21 comments
Read more

[MW:36169] Cold Bending Qualification

By Materials & Welding
Dear Experts,  Can anyone share the inspection requirements or a qualification procedure for cold bending? Our client spec states only the requirements for induction bending and would like to know your opinion on the cold bend inspection requirements. The code of construction is B31.3, Max. 5D bends, A106 SS 316L.  Thanks in Advance. -- https://materials-welding.blogspot.com/ https://www.linkedin.com/groups/122787 --- You received this message because you are subscribed to the Google Groups "Materials & Welding" group. To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com . To view this discussion visit https://groups.google.com/d/msgid/materials-welding/1be61cc3-e9c9-4a5f-834d-e8485e248432n%40googlegroups.com .
Post a Comment
Read more

[MW:30043] Weep hole

By Materials & Welding
If weep hole is not provided in dummy pipe before welding What will happen??? -- https://materials-welding.blogspot.com/ https://www.linkedin.com/groups/122787 --- You received this message because you are subscribed to the Google Groups "Materials & Welding" group. To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com . To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/da251ee6-fa7f-4851-b876-cdb3834ae341%40googlegroups.com .
Post a Comment
Read more