Re: FW: [MW:4371] DSS REPAIR WELDING PROCEDURE

Dear Rutvik and Pradip,

As addition on the remarks of Pradip especially regarding "you may use
cast material" the following: Welding procedure qualifications
according to ASME section IX are not allowed as base for WPS
qualifcation in casting repairs according to ASTM A995. This
specification clearly mention under chapter 11 that all procedures and/
or welders need to be qualified according to ASTM A488. This
specification is especially for casted materials and requires
qualification on casted base materials only so often this is not the
case for ASME section IX qualifications. Chemical composition also
need to be similar to the material to be weld. If the comapny has no
qualification according the ASTM A488 they are not allowed to execute
any repair.

Best Regards,

Herman Pieper

On 24 feb, 19:10, <pgosw...@sympatico.ca> wrote:
> Hi Rutvik,
>
> ASTM A 995 GR.4A(DSS) is 22Cr-5Ni-Mo-N(UNS-J92205) duplex casting. The matching chemistry for this product is ASME  -SA-240 S31803 (in plate),  and in pipes SA-790. However many a times castings would have a lot of unbalanced chemistry due many factors e.g.: manufacturing technique, shapes, irregular cooling rates, responses to heat treatment etc. That's why welding on duplex castings are always more difficult then welding on plates or  pipes.
>
> Duplex stainless steels are very good alloys  with a good  combination of enhanced mechanical properties and corrosion resistance when properly balanced in composition and properly heat treated. Generally they develop a range of approximately 30 to 60% ferrite with the balance austenite.
>
> In your case, the manufacturer have a welding procedure which meets the requirements of ASME Sec-IX. But client's requirements or any specification requirement are over and above the code requirements, due to the facts that they are service application specific. If client requires  the flowing tests as mentioned below, your vendor (casting shop) has to redo the qualification test. It may be done  by preferably weld a  supplementary test coupon to the existing PQR and performing tests such as ferrite count,  pitting corrosion , detection of sigma phase and other intermetallic phases. It is not necessary to repeat the mechanical tests.
>
> In order to perform a supplementary weld coupon:-
> ·         Weld a test coupon following  exactly the welding parameters of existing and qualified PQR. Duplex S.S requires a good control on welding heat input.
> ·         You may use casting materials (if available as spare) or plate or pipes of equivalent composition and properties.
> ·         Perform ferrite count - ASTM-E-562
> ·         Detection of any intermetallic/sigma phases-ASTM-E-923
> ·         Pitting Corrosion Test- according to ASTM G-48
> ·         Meet any other test requirements as asked by  your client.
>
> ASTM –A-995 Clause -12. recommends stress relieving of duplex S.S castings, if the weld repair is major (i.e. if the depth of repair is over 20% of actual wall thickness or 1 inch, whichever is smaller). Should the weld repair calls for stress relieve as per A-995, then a completely new PQR shall be established, meeting  all Sec-IX mechanical tests, plus the other tests as mentioned above. Usually ASTM-A-488 is the guiding document for qualification of welding procedures for casting repair.
>
> Note : ASTM-A-995 –Supplementary requirements S-1 through S-51  describes some of the additional testing as required by your client.
>
> Hope my response clarifies the issue.
>
> You may download these free documents for your reference:-
> ·          http://www.imoa.info/_files/stainless_steel/Duplex_Stainless_Steel_2d.... This is a comprehensive document on duplex S.S.
>
> Thanks.
>
> Pradip Goswami, P.Eng.
> Welding & Metallurgical Engineer/Specialist
> Component Integrity Section.
> Engineering and Training Services
> Ontario Power Generation Inc.
> Res:-88,Garth Trails Crescent
> Hamilton,Ontario, L9B2X1,Canada
> Email-pgosw...@sympatico.ca
> Email-pgosw...@quickclic.net
> Tel-905-679-9677
>
>
>
> -----Original Message-----
> From: materials-welding@googlegroups.com
>
> [mailto:materials-welding@googlegroups.com] On Behalf Of rutvik dixit
> Sent: Tuesday, February 23, 2010 12:45 PM
> To: materials-welding@googlegroups.com
> Subject: [MW:4366] DSS REPAIR WELDING PROCEDURE
>
> Hi everyone,
> I need to inspect the castings of ASTM A 995 GR.4A(DSS). Now mfr. is having the approved/qualified wps for repair work. This material (castings) is
> having other requirements like ferrite content, pitting corrosion resistant test, sigma phase, total of intermetallic phases. The qualified wps doesn't consist these metallurgical tests, but having all mechanical and impact test. can mfr. go ahead with this wps for repair work? wps is having any
> relationship with these type of metallurgical tests?
>
> With regards,
> Rutvik
>
>       The INTERNET now has a personality. YOURS! See your Yahoo! Homepage.http://in.yahoo.com/
>
> --
> To post to this group, send email to materials-welding@googlegroups.com
> To unsubscribe from this group, send email to
> materials-welding-unsubscribe@googlegroups.com
> For more options, visit this group's bolg athttp://materials-welding.blogspot.com/
> The views expressed/exchnaged in this group are members personel views and
> meant for educational purposes only, Users must take their own decisions
> w.r.t. applicable code/standard/contract documents.
>
> THIS MESSAGE IS ONLY INTENDED FOR THE USE OF THE INTENDED RECIPIENT(S) AND MAY CONTAIN INFORMATION THAT IS PRIVILEGED, PROPRIETARY AND/OR CONFIDENTIAL. If you are not the intended recipient, you are hereby notified that any review, retransmission, dissemination, distribution, copying, conversion to hard copy or other use of this communication is strictly prohibited. If you are not the intended recipient and have received this message in error, please notify me by return e-mail and delete this message from your system. Ontario Power Generation Inc.- Tekst uit oorspronkelijk bericht niet weergeven -
>
> - Tekst uit oorspronkelijk bericht weergeven -

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

No comments:

[MW:34820] RE: 34813] Clarification in Rate of heating and cooling.

Hello,   Please see the response below.   Regards.   P. Goswami, P. Eng, IWE.   From: materials-welding@googlegroups.com <materials-weld...