Re: [MW:4300] AFFECT POLARITY IN HEAT INPUT

By Materials & Welding
Agree with George. At DCEP the electrone will flow from tungsten to base metal and at DCEN will flow from base metal to tungsten. This electron flow will affect to the penetration.

Regards,
Endri

Sent from my BlackBerry®

From: george.dilintas@gr.bureauveritas.com
Date: Fri, 12 Feb 2010 23:34:31 +0100
To: materials-welding<materials-welding@googlegroups.com>
Subject: Re: [MW:4294] AFFECT POLARITY IN HEAT INPUT

It is because of the difference of the electrons flow I think

  From: Ali Asghari [asghariali@rocketmail.com]
  Sent: 11/02/2010 23:44 PST
  To: materials-welding@googlegroups.com
  Subject: [MW:4291] AFFECT POLARITY IN HEAT INPUT


Hi All
all know that heat input is independent from polarity.but  i see in GTAW that in DCEN ,70%HEAT generated in arc concentrated in parent metal & in DCEP 30% HEAT concentrated in base metal.
can anybody clarify it?
regards.

Comments

Post a Comment

Popular posts from this blog

Materails FAQs

By Materials & Welding
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...
21 comments
Read more

[MW:36169] Cold Bending Qualification

By Materials & Welding
Dear Experts,  Can anyone share the inspection requirements or a qualification procedure for cold bending? Our client spec states only the requirements for induction bending and would like to know your opinion on the cold bend inspection requirements. The code of construction is B31.3, Max. 5D bends, A106 SS 316L.  Thanks in Advance. -- https://materials-welding.blogspot.com/ https://www.linkedin.com/groups/122787 --- You received this message because you are subscribed to the Google Groups "Materials & Welding" group. To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com . To view this discussion visit https://groups.google.com/d/msgid/materials-welding/1be61cc3-e9c9-4a5f-834d-e8485e248432n%40googlegroups.com .
Post a Comment
Read more

[MW:30043] Weep hole

By Materials & Welding
If weep hole is not provided in dummy pipe before welding What will happen??? -- https://materials-welding.blogspot.com/ https://www.linkedin.com/groups/122787 --- You received this message because you are subscribed to the Google Groups "Materials & Welding" group. To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com . To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/da251ee6-fa7f-4851-b876-cdb3834ae341%40googlegroups.com .
Post a Comment
Read more