Re: [MW:24340] Failure Analysis // failure during Hydrotesting

Thanks, it is very useful.
 
BR,
Shashank C Vagal 




From: Raghuram Bathula <raghurambathula@gmail.com>
To: Materials-Welding <materials-welding@googlegroups.com>
Sent: Sunday, 21 February 2016 3:20 PM
Subject: Re: [MW:24335] Failure Analysis // failure during Hydrotesting

few of them could be Material itself, cracks arising out airstrikes or during fabrication, hydrotest temperature etc. refer below link

http://products.asminternational.org/fach/data/fullDisplay.do?database=faco&record=961&trim=false

On 21 February 2016 at 12:51, 'Shashank Vagal' via Materials & Welding <materials-welding@googlegroups.com> wrote:
Dear all,
Please suggest what could have caused this pipe failure after Hydrotesting..... Consider all general conditions as all details are not known yet
 
BR,
Shashank C Vagal 

--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CADxVub%3D95qOYzcrJcn-ZNSjn-ukjDrTRZO3qrby9oJxE0MtBDA%40mail.gmail.com.
For more options, visit https://groups.google.com/d/optout.


No comments:

Re: [MW:35289] Welding consumable for S355J2WP material

S355 J2 WP  is a weathering structural steel  It has better atmospheric corrosion resistance. Use E 8018 - W1/W2  Electrodes This is regular...