Re: [MW:24301] P-91 to SS Welding

it is not advisable to use 309 because 309 weld metal  may not be  suitable for service/pwht  temp above 370 C 

THANKS & BEST REGARDS,

KG.PANDITHAN, IWE,  AWS-CWI, CSWIP 3.1,

CONSULTANT-WELDING & QUALITY

On Mon, Feb 15, 2016 at 4:18 PM, George Dilintas <dilintas@gmail.com> wrote:

the final welding is better to do with grade 309 filler metal (in order to avoid low FN and thus hot cracking)

2016-02-11 11:08 GMT+02:00 pradip kumar Sil <pradipsil@gmail.com>:

Dear Sir,

Thanks in advance.

As per my understanding :

 We will do buttering the P-91 pipe around 5 mm with PRE HEAT + POST HEAT +PWHT by  filler wire ERNiCr-3. Afterwards fit-up will be done with SS pipe & continue welding without preheating +postheating +pwht.

Correct me if i am wrong.

Regards,

On Mon, Feb 8, 2016 at 6:11 PM, <dilintas@gmail.com> wrote:

If your Code is ASME you need to PWHT whatever the thickness is. So the best practice is to do buttering and then PWHT. Once PWHT completed you weld to 316. 

The thickness of the buttering should be such that the haz of the second weld does not fall on P91. I would suggest 5 mm

Sent from my BlackBerry 10 smartphone.

From: pradip kumar Sil Sent: Δευτέρα, 8 Φεβρουαρίου 2016 - 14:56 To: materials-welding Reply To: materials-welding@googlegroups.com Subject: [MW:24251] P-91 to SS Welding

Dear Expert,

We have to weld P-91 Material to 316 (SS) material with ERNiCr-3 filler Wire Socket Weld.

My question is needs to do buttering  the P-91 material if required how much layer we Need ?

During  & After buttering needs to conduct preheating & Post heating ?

During & after welding socket weld  only P-91 side or both side  we will conduct preheating +post heating + PWHT

Thanks in advance.

Regards

--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAB%3DAs8n21J7FMEX31_hSbAX6DsXuA_stk1djcB7viooW3Lk-zA%40mail.gmail.com.
For more options, visit https://groups.google.com/d/optout.

--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.

To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/20160208131119.6713429.35185.1712%40gmail.com.
For more options, visit https://groups.google.com/d/optout.

--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAB%3DAs8myMeHao4drWHtqsTAFKQ47C5Fp965A8O%3D4S-MLOqijzQ%40mail.gmail.com.

For more options, visit https://groups.google.com/d/optout.

--

Georgios Dilintas

A.I.S, A.N.I, IRCA Lead Auditor

Welding, Stress Analysis, Corrosion, QA/QC, Failure Analysis

--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAPOi40DH%2BnS_toBWvm84Kj9bsPnVTJO572RPkn8FhWWXmpfeqg%40mail.gmail.com.
For more options, visit https://groups.google.com/d/optout.

--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAJzm4eOdP1kLJkM_J5VxNdZL_4xx%3DbpTDCCaRES9W3ef2GxgJg%40mail.gmail.com.
For more options, visit https://groups.google.com/d/optout.