[MW:24358] RE: 24355] Impact Test & cooling Rate-Preheating (carbon steel)

For structural steels and pipeline steels (carbon and carbon-manganese steels) the preheat requirement increases with combined thickness. See EN 1011:Part 2. The objective is to slow the cooling rate to prevent the formation of martensite which is hard and brittle and susceptible to hydrogen cracking.

 

Alan Denney

AKD Materials Consulting Ltd

 

From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] On Behalf Of Mohd Siraj
Sent: 22 February 2016 09:22
To: Materials & Welding <materials-welding@googlegroups.com>
Subject: [MW:24355] Impact Test & cooling Rate-Preheating (carbon steel)

 

Dear all,

 

Background: 

impact testing is more critical for less(low)thickness than higher thickness.

 

Reason  : 

fine grain form during fast cooling and course grain form during slow cooling.

 

Question is:

Preheating use to lower the cooling rate for higher thickness.

So lower the cooling rate means form the course grain,course grain lower the toughness.

 

Preheating contributing to lower the toughness?

 

 

 

 

--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/3247d39d-f53a-4bc4-aee8-79f73a1d95d8%40googlegroups.com.
For more options, visit https://groups.google.com/d/optout.

No comments:

Re: [MW:35289] Welding consumable for S355J2WP material

S355 J2 WP  is a weathering structural steel  It has better atmospheric corrosion resistance. Use E 8018 - W1/W2  Electrodes This is regular...