Thank you Pradip Sir

Thank you so much for your valuable advice. would definately bring in notic to the EIL Standard Development group. Kindly clarify one more doubt, as we know that P-91 is poor to weld corrosion, what could be the possible corrosion and failure mechanism if we use ER 309 and how usage of ER NiCr3 helps

Warm Regards

Arunabh 

On Tuesday, May 27, 2014 4:42:10 PM UTC+5:30, ARUNABH BERA wrote:

Dear All

Kindly clarify the doubts:

Sir in Ethylene Cracker Furnace at one of the Petrochemical Plant, we have a hook-up between P-91 and SS304H. Here we are using ER309 as the filler.

Is it acceptable, if not what can be the probable problems associated with the filler selection and what are the solutions 

Regards

Arunabh

Engineers India Limited

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
 
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
For more options, visit https://groups.google.com/d/optout.