Re: Re: [MW:28988] IF ans IFD as per API 1104

So, yes in your case after ensuring process and back strip material, possible what you have interpretated, so in this case the root causes are already been proactivated through the subject email and hence correction shall be done.

Re: Re: [MW:28730] Auto Welding Copper back up strip fused with Root run

Thanks.

---

Regards,

Mohamed Muneeb Mahaboob

CSWIP 3.2-89247/2 

IRCA-9001:2015 LA

ASNT-NDT-L2-RTFI-RT-UT-MT-PT.

SAP#:70021650 APs:JAPID, QCS & QCI.

E muneebslsa@gmail.com M +91-636-955-7189

''If you know any art by any means then SCULPT IT - no matter how cheap or useless it is - JUST SCULPT IT, you will never know when experts will be on demand'' 

 

From: riaz rafeeque

Date: 2019-01-25 12:16

To: materials-welding

Subject: Re: [MW:28973] IF ans IFD as per API 1104

GMAW Process with Cupper back strip

Base Metal : API 5l X70 , 6.62 mm thick, Groove is U with 2 mm root face , 0 mm root gap

On Fri, Jan 25, 2019 at 10:44 AM Mohamed Muneeb <muneebslsa@gmail.com> wrote:

It doesn't seem like to be a cupper. What is the bm and process used?

Regards

Muneeb

On Thu, Jan 24, 2019, 9:18 AM riaz rafeeque <riaz.rafeeque@gmail.com> wrote:

We did an RT to verify the presence of IFD . But not getting IfD on RT. 

In addition we noticed bright indication , which may be cupper pick up in root. 

Client representative  interpretated this  as Cupper Pick Up

Experts pls advice. 

On Sun, Jan 20, 2019, 11:34 AM Ramin Kondori <raminkondori@gmail.com wrote:

I read the comments.

Why don't you correct your welding procedure...?

All these discussions aside, finally your meat is under your client's teeth.

So I recommend you first to correct the issue. This way you will have more of your client support.

But if you don't and just try to justify, it will make them more upset. Believe me, I have been the client's inspector all my career.

Tell me about the welding procedure. 

Regards

Ramin  Kondori

Sr. QA/QC & Welding Engineer

-----------------------------------------------------------

PG-Dip. in Welding Engineering (IWE  AT  0070)

BSc. in Civil Engineering (IUT)

BGAS Painting Inspector

ASNT Level I&II

                        

On Wed, Jan 16, 2019 at 7:24 PM Ri@z <riaz.rafeeque@gmail.com> wrote:

Dear All,

Our Pipeline specification not accepting Incomplete Fusion .In case of incomplete fusion weld shall be rejected and re-welded.

But according to API 1104, IF and IFD are different . So is it required to reject both IF and IFD as both are incomplete Fusion?

Please help me with advice 

I am using AUT for the inspection and 70 % of joints are detecting either IF or IFD 

With Regards

Riaz 

Pls help me 

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to a topic in the Google Groups "Materials & Welding" group.
To unsubscribe from this topic, visit https://groups.google.com/d/topic/materials-welding/lJ1fIfkP9Lc/unsubscribe.
To unsubscribe from this group and all its topics, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to a topic in the Google Groups "Materials & Welding" group.
To unsubscribe from this topic, visit https://groups.google.com/d/topic/materials-welding/lJ1fIfkP9Lc/unsubscribe.
To unsubscribe from this group and all its topics, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.