-- I have revived comments from CSD my WPS.
I have mentioned with Impact requirement in WPS, as per PQR.
Please refer the below details WPS and PQR DATA.
| WPS | ||
| Welding Process : GTAW | ||
| CODE: IX,ASME : B31.3 &SAES- W-11 | ||
| QW-403 | ||
| P No :8 To Group No:1 | P No :8 To Group No:1 | |
| Base metal Thickness Range : | Groove: 2.99mm to 11.96 | |
| QW-404 | ||
| GTAW | ||
| SFA No - | 5.9 | |
| AWS No- | ER316L | |
| PQR | ||
| Base Metals : SA312 TP 316L to SA312 TP 316L | ||
| P No :8 To Group No:1 To P No :8 To Group No:1 | ||
| Thickness : 5.98mm | ||
| Filler Metals: ER316L | ||
| Pre heat Temp : 21°C Min | ||
| Inter pass Temp : 126°C Max | ||
Query : As per SAES -W-011 clause no -7.4.13.2 not required Impact test and i have to change Base metal thickens 1.5mm to 11.96mm.
Please awaiting for your reply.
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.
No comments:
Post a Comment