Dear Friend,

Purpose of post heat is to DIFFUSE hydrogen after welding , for this purpose we hold our joint at 93-80 degree for 1 hour after completion of welding.

PWHT always Performed below Lower Transformation Temperature, PWHT and Post Heat is different things.

Kind Regards

On Tue, Jan 29, 2019 at 2:27 PM George Dilintas <dilintas@gmail.com> wrote:

Most propably your client wants you to perform a hydrogen bake-out treatment

Στις Δευ, 7 Ιαν 2019, 08:58 ο χρήστης muneebslsa@gmail.com <muneebslsa@gmail.com> έγραψε:

Hi All,
Client specification calls for post weld baking/heating (not stated as PWHT) of a P No.1 material after welding for a specific reason. Does it consider a PWHT condition as per ASME Sec IX QW-407.1(a) Point#2, i.e PWHT below lower transformation temperature? If it is considered as PWHT as per the clause above, then would a PQR with 200 Deg C PWHT qualifies to perform PWHT on the weld at 600 Deg C which is below the lower transformation temperature of P No.1 keeping all other essential variables same. Note: Though there is an interpretation available (IX-04-03), it doesn't state the answer instead it refers to QW-407.1 (throwing the ball away wisely).

Originally posted in Linkedin

by

Ishack Mohammed Ismail
• 1st
Technical Representative at ABS Consulting
4d • Materials-Welding

Regards,
Mohamed Muneeb Mahaboob
CSWIP 3.2-89247/2
IRCA-9001:2015 LA
ASNT-NDT-L2-RTFI-RT-UT-MT-PT.
SAP#:70021650 APs:JAPID, QCS & QCI.
E muneebslsa@gmail.com M +91-636-955-7189
''If you know any art by any means then SCULPT IT - no matter how cheap or useless it is - JUST SCULPT IT, you will never know when experts will be on demand''

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.

Respected Sir,

Please find the enclosed file.

Bilal Arshad Wahla

P.W.H.T Engineer

SEPCO Electric Power Construction Corporation

Saudi Aramco JAZAN IGCC Power Block Project (EPC-4)

Jazan Economic City, KSA

Mobile: +966 591317207

Email: bilalwahla.047@gmail.com

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.

Re: [MW:34105] SA266 GR4N 4 Cycle SPWHT

Hi, You are correct, Minimum refers to the one cycle for which this part will expose until final work shop PWHT. hence mill test certificate shall include this. Max. SPWHT, refers to additional cycles of heat treatment that are reserved for future repairs during equipment lifetime. Again, these simulated no. Of cycles shall be specified in MTC. The idea is we need to make sure that steel mechanical properties are not compromised upon exposure to multiple repairs (i e 4 cycles in your case). One could say, if steel is subjected to 4 cycles and is ok, then it should by defacto be good for one cycle, yet, this is wrong assumption cause mechanical problems and microstructure of materials varies accordingly based on no. Of cycles for which material will expose. This is apparent in alloy steel and especially for impact test values as an example. In your case, this forged CS with properties before PWHT can be understood to be " as forged" condition (i.e. Wit...

Materails FAQs

Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change. Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...

Materials & Welding

Search This Blog