595 for pwht , 915 normalizing
On Sun, Nov 25, 2018 at 9:35 AM Souravbohray <ermechsouravbohray@gmail.com> wrote:
ucs 56 adress minimum holding temprature eg- for Pno 1 its 595 C. can i hold it at temp 915℃ because after 915 there will be change from alpha phase to gamma and bcc structure to fcc.
and one more point from 770c there will be also change from magnetic to non magnetic property.
i take refference from iron carbon diagram.
--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.
No comments:
Post a Comment