Re: [MW:28601] STEEL GRADES S460NL & S500ML

By Materials & Welding
N?

On Thu, Nov 8, 2018 at 8:56 AM Kannayeram Gnanapandithan <kgpandithan@gmail.com> wrote:
M---Thermomechanically treated. Generally there are 3 impact requirements in joules. J, K, L. 27joules for J. 40joules for K & 60joules for L at tested temp. For more understanding pl ref EN 10020

On Wed, 7 Nov 2018 6:03 pm Hani Al Masry <hanyonalfy@gmail.com wrote:
HOW ABOUT   S500ML 
What is M and L OR NL OR ML? 
Can you send me the copy of standards of each one?
also EN 10025-4:2004  and DIN EN 10025-3 which you refer to?

Regards,
H.A
 

On Tue, Nov 6, 2018 at 10:53 AM rajesh kaswala <rajeshkasvala@gmail.com> wrote:
  S460NL acc. to DIN EN 10025-3 Mat.no. 1.8903 S460NL is a weldable, normalised steel for steel constructions, with high yield strength combined with high toughness to save weight in use.
 Delivery with certificate 3.1 to DIN EN 10204. 
Chemical composition (heat analysis %) Grade C max. Si max. Mn P max. S max. Al min. Cr max. Mo max. Cu max. Ni max. V max. N max. Nb Ti S460NL 0,20 0,60 1,00- 1,70 0,025 0,020 0,020 0,30 0,10 0,55 0,80 0,20 0,025 0,05 % 0,05% 
Mechanical properties in delivery condition Tensile testing on transverse specimens at room temperature Grade R m (MPa) ReH (MPa) A5 (% min.) 
Thickness mm  100 > 100  200  16 > 16  40  40  63 > 63  80 > 80  100 > 100  150 S460NL 550 - 720 530 - 700 460 440 430 410 400 380 17 
impact values (KV) carbon equivalent values (CEV) transverse 27 Joule -50°C  63 mm 0,53 longitudinal 16 Joule -50°C  63  100 mm 0,54 

  regard
rajesh

On Sun, Nov 4, 2018 at 8:29 PM Hani Al Masry <hanyonalfy@gmail.com> wrote:
Dear Exerts 

what is Steel Grades S460NL & S500ML Are this is CS or it is alloy steels like HARDOX , WELDOX and now they call it Domex?

what is it is specification ? standards? recommended usage and applications?

Regards,
H.A

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.

Comments

Post a Comment

Popular posts from this blog

Re: [MW:34105] SA266 GR4N 4 Cycle SPWHT

By Materials & Welding
Hi,  You are correct, Minimum refers to the one cycle for which this part will expose until final work shop PWHT. hence mill test certificate shall include this.  Max. SPWHT, refers to additional cycles of heat treatment that are reserved for future repairs during equipment lifetime.  Again, these simulated no. Of cycles shall be specified in MTC.  The idea is we need to make sure that steel mechanical properties are not compromised upon exposure to multiple repairs (i e 4 cycles in your case).  One could say, if steel is subjected to 4 cycles and is ok, then it should by defacto be good for one cycle, yet, this is wrong assumption cause mechanical problems and microstructure of materials varies accordingly based on no. Of cycles for which material will expose. This is apparent in alloy steel and especially for impact test values as an example.  In your case, this forged CS with properties before PWHT can be understood to be " as forged" condition (i.e. Wit...
Post a Comment
Read more

Materails FAQs

By Materials & Welding
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...
21 comments
Read more

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

By Materials & Welding
Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change.   Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...
Post a Comment
Read more