This is bulging?
A: Yes
any welded valves adjacent which is 1500 or 2500 ratings?
A: No, but there is a heavy piping above and restriction below.
Did you carriedout postheating after welding?
A: Yes, 2 hours @760°C
Did you had bolt torquing either side fixed strongly?
A: It doesn't have any flanges.
Is there any distortion after welding and carriedout PWHT without any rectifications?
A: No, distortion appeared after PWHT.
Or Modifcations done for repairs (Cutout or partial repairs) before PWHT?
A: Yes, it was done partial repair before PWHT.
--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.
A: Yes
any welded valves adjacent which is 1500 or 2500 ratings?
A: No, but there is a heavy piping above and restriction below.
Did you carriedout postheating after welding?
A: Yes, 2 hours @760°C
Did you had bolt torquing either side fixed strongly?
A: It doesn't have any flanges.
Is there any distortion after welding and carriedout PWHT without any rectifications?
A: No, distortion appeared after PWHT.
Or Modifcations done for repairs (Cutout or partial repairs) before PWHT?
A: Yes, it was done partial repair before PWHT.
--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.
Comments