its on face side or root side?

On Sunday, September 9, 2018 at 6:32:32 AM UTC+3, Hrushikesh Sangamnerkar wrote:

Dear expert,

Problem observed:

After welding Black spots are seen on weld. These black spots are not removed even after pickling & passivation.

MOC - SS 347

Filler metal - ER347

Dia. - 1.2mm

Gas used Argon + 2% CO2

Mode - Pulse

Flow rate - 10lpm

Note:

EDS analysis of weld doesn't show any carbon content.

Pl suggest some remedy by which these black spots can be avoided.

Regards,

--