[MW:28262] Re: Cracked on Welding Joint P91 to 50 Cr 50 Ni

Thanks. the  image is interesting.

However, there is no crack in the welding. and its looks away from typical HAZ area. The reason might be high restraint.

Thanks & regards

Sandeep Kumar

On Tuesday, August 14, 2018 at 3:17:11 PM UTC+3, nguyen tuan wrote:

Dear Expert,

The Cracking found on  welded P91 to 50 Cr 50 Ni with welding consumable E NiCrFe-3 

If anyone has the comment on this

Thanks ,

Best Regards,

Nguyen ANh Tuan

--