Re: [MW:28261] preheating

Thanks for reply.

My next question is if cooling rate is fast it's mean cooling rate is high or sudden cooling due to which cracking is occur we do preheating.basically martensitic structure form.

Due to preheating material become more hard than brittle than cracking.

So we have to heat preheating for thickness above 25mm because cooling rate is high in higher thickness ?????

If hydrogen amount is high in weld than crack will come after cooling.so to get hydrogen out from weld during we give more to hydrogen to get out from weld by increasing cooling time by preheat???

How to decide for which material we have to use low hydrogen electrode because suppose we have material above 25 mm thick we use 6013 and 7019, 6011.so how to decide were to use 7018 ,hydrogen source is moisture it will come for all material y donor use 7018 for all material to reduce amount of hydrogen by use of 7018.

Please reply my inspector hold my WPS he wants reason y I m not using 7018 for all material

On Mon, 10 Sep 2018, 3:41 pm CHITTARANJAN BHIWANDKAR, <crbhiwandkar.smspl@gmail.com> wrote:

Thanks/Regards,Preheating is the process applied to raise the temperature 

of the parent steel before welding. It is used for the following main reasons:

·         The slower cooling rate encourages hydrogen diffusion from the weld area 

by extending the time period over which it is at elevated temperature 

(particularly the time at temperatures above approximately 100°C) 

at which temperatures hydrogen diffusion rates are significantly higher than at 

ambient temperature. The reduction in hydrogen reduces the risk of cracking.

·         To slow the cooling rate of the weld and the base material, potentially resulting in 

softer weld metal and heat affected zone microstructures with a greater resistance 

to fabrication hydrogen cracking.

C.R.Bhiwandkar

Supreme Megastructures Pvt. Ltd.

Cell No.:-+919867139337

On Sun, Sep 9, 2018 at 3:31 PM Souravbohray <ermechsouravbohray@gmail.com> wrote:

what is use of preheating ?
how can control rate of cooling by preheating ? by apply of heat how cooling rate can be control ?
by preheat hardness increase or decrease?

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to a topic in the Google Groups "Materials & Welding" group.
To unsubscribe from this topic, visit https://groups.google.com/d/topic/materials-welding/rBiIayd4k_8/unsubscribe.
To unsubscribe from this group and all its topics, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.