Re: [MW:24191] Hardness Of P-91 Material

Dear friend
Do heating and cooling rate 60 degree per hour and do proper booth preparation with teen sheet and do not open up to 24 hours after pwht complete
We are doing 52 mm thick p91 joints
Mansukh Satashiya

On Jan 30, 2016 10:43 AM, "pradip kumar Sil" <pradipsil@gmail.com> wrote:

Dear Everybody,

Some of our P-91 Joints( Weldment) are coming hardness value around 300HB in the HRSG Unit.

 Joints thickness is 18 mm & 20 mm & we did PWHT 2 hours holding time at 710 degree centrigrade also we did 150 degree heating rate ,120 degree cooling rate.

Can you pls suggest us this hardness value  is acceptable in the HRSG unit. If not pls suggest me how to recover.

Regards,

Kumar

--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAB%3DAs8mJXj9twE50bbG4-%2Bb-_35XPHeuAZ97xUD5n1Aq7TR21Q%40mail.gmail.com.
For more options, visit https://groups.google.com/d/optout.

--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAMJpn0VumJGH4-OaN%3DM_QxczWCeR%3DZxMeTgU9Q%3DcyNW9K4VHyQ%40mail.gmail.com.
For more options, visit https://groups.google.com/d/optout.