[MW:24189] Effect of brazing temp. on Pure Iron

Dear All,

I have an application of using Pure Iron (Aramco Grade 4), which will undergo a brazing cycle (in vacuum furnace) upto 1060 Deg C.

Query is: Will there be any impact on the mechanical properties at room temperature. Cooling is furnace cooling.

Chemical composition are:

C 0.010   
Mn 0.060
P 0.005
S 0.003
N 0.005
Cu 0.030
Co 0.005
Sn 0.005
   
Typical hardness: 90-95 HB


Thanks in advance.

Regards,
Jaydeep

--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CA%2BY7Lqdoz9vF9Gva_QXZjU3pMY%3DXPzfRKtysabWR8oaAhGmzZg%40mail.gmail.com.
For more options, visit https://groups.google.com/d/optout.

No comments:

Re: [MW:35289] Welding consumable for S355J2WP material

S355 J2 WP  is a weathering structural steel  It has better atmospheric corrosion resistance. Use E 8018 - W1/W2  Electrodes This is regular...