[MW:10058] Difference between impact testing by ASTME23 and ASTM A370

Dear all, 

I have a procedure in which impact testing should have been done as per  ASTM A370 but it has been done as per ASTM E23

Is there any difference between the standard on how the impact tests are conducted? Would the difference effect the final values?
tha material was UNS 31803 pipe and was tested at minus 50 degree centigrade.

Thanks

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
By -

No comments:

Post a Comment

Subscribe to: Post Comments (Atom)

Re: [MW:35488] Re: 2411] Re: FW: 2390] Aluminium welding Data

In Aluminium welding, Cleaning Aluminium oxide, hydrated oxide to be cleaned mechanically & by ARC also.  Al2O3 has got melting temperat...

  • Materails FAQs
    Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? ...
  • RE: [MW:5585] Buttering of weld joints
    Definition of buttering from ASME Section IX, QW/QB-492 Definitions:   Buttering:  the addition of material, by welding, on one or bot...
  • WELD AND WELDING SYMBOLS
    Section I. PRINT READING 3-1. GENERAL a. Drawings . Drawing or sketching is a universal language used to convey all necessary information to...