Re: [MW:10005] TECHNICAL CLARIFICATION 1- WPS AND PQR

Dear Mr.Moin..
 
1. Yes you have to mention each pass welding thickness when you are carrying out the welding of  particular joint  with two types of welding (like GTAW+SMAW, GMAW+SAW ,, etc) Each welding pass thickness qualified multiplied by two will give you the maximum thickness for which the particular welding process is allowed..
 
2. Not required
 
3. With single pass also you should monitor the interpass temperature..
 
br,
msms


 
On Wed, Feb 23, 2011 at 5:00 PM, Moin - QC <Syed.Moin@gerabgroup.com> wrote:

Dear friends,

I have few question related to WPS, I am trying to check whether it complies to XI though I am not  CSWIP certified or a welding engineer, appreciate if you could provide some information to me on the  following

1-      Is it mandatory to mention the qualified weld metal thickness on WPS, if yes  what should be qualified weld metal thickness for a test coupon 9 mm thick and welded by GMAW and SAW process , should it be 2t as per table QW 451.1?  How to find '' t'' before doping welding?

2-      Is it mandatory to mention the lot number of flux& wire on the WPS, if No could you please provide me reason?

3-      My understanding is if the welding is single pass than interpass temperature does not come into picture is it true?

Thanks & Regards
Syed Moin                               


______________________________________________________
CONFIDENTIALITY NOTICE: This electronic mail transmission may contain information that is confidential, privileged, proprietary, or otherwise legally exempt from disclosure and is intended only for the use of the recipient named above. We do not waive confidentiality in the event this mail was transmitted wrongly. If you have received this communication in error, and are not the intended recipient, you are hereby notified that you are prohibited from reading, printing, copying, or disseminating this message, any part of it, or any of the attachments it may carry. If you have received this message in error, please destroy all electronic and paper copies and notify the sender immediately of the inadvertent transmission. We would like to advise you that we would not waive any of our privilege for taking action against you in the event the confidentiality of this message has been compromised. Thank you for your cooperation
________________
This email has been scanned by the MessageLabs Email Security System.
For more information please visit http://www.messagelabs.com/email
______________________________________________________________________

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

No comments:

[MW:34820] RE: 34813] Clarification in Rate of heating and cooling.

Hello,   Please see the response below.   Regards.   P. Goswami, P. Eng, IWE.   From: materials-welding@googlegroups.com <materials-weld...