Re: [MW:31627] Crack in vessel due to over pressure

Hi,

Design calculations will let you know if it is due to over pressure,

Regards 

On Tue, 27 Oct 2020, 15:45 Muhammed Ibrahim PK, <ibratech@gmail.com> wrote:
Gents, 

Is there any option to find out if the vessel is cracked because of over pressure at site by mistake. 

If we perform a tensile test across the crack area, can we get any clue if grains are already permament deformed due to over pressure? 

Or is there any other metallogaraphic method can we employ? 

Reg, 
Ibrahim

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CALOPgmOdwJJ9v2kp-NWhkvQsj89n_9c1nNh5P_hJk_csUEmz%3Dg%40mail.gmail.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAOi%3DZp_tDfmNV4Ox%3DvWd8PTTs4%2BXH%2BU4FuLhhX_J%3Dh8V_taSEA%40mail.gmail.com.

No comments:

Re: [MW:35289] Welding consumable for S355J2WP material

S355 J2 WP  is a weathering structural steel  It has better atmospheric corrosion resistance. Use E 8018 - W1/W2  Electrodes This is regular...