Use the highest welding speed possible. The faster the weld is conducted, the faster the cooling rate and the less time the weld is in the hot cracking temperature range.
-- Try to use welding and assembly sequences and techniques that minimize restraint, reduce residual stress and produce welds of acceptable profile.
This picture shows two fillet weld terminations in the corner of a welded structure. Cracking is visible in both termination craters. Also cracking is visible along the center of both welds. The reason for this hot cracking is undesirable weld profile caused by poor welding technique. The reduction in throat thickness at the termination and for a portion of the fillet weld has allowed the stresses developed during welding to fracture the weld.
Thanks & Regards,
aslab a khan
On Tue, Oct 31, 2017 at 3:13 PM, Amul Raj <win.amul@gmail.com> wrote:
Dears Experts,--Hydro cracker Unit, Heater Radial coil welding base material 347H and Filler wire ER347H(Metrode) Size 4' x 13.49 ThicknessWhen we start the welding, getting crack in the weld stop and start pointPlease advise meRegards,Amul Raj T
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com .
Visit this group at https://groups.google.com/group/materials-welding .
For more options, visit https://groups.google.com/d/optout .
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.
No comments:
Post a Comment