U can go ER NiCrFe6 also
On 05-Aug-2017 9:21 PM, "PREM SHANKARDUTT NAUTIYAL" <prem_nautiyal@rediffmail.com> wrote:
This message is eligible for Automatic Cleanup! (prem_nautiyal@rediffmail.com) Add cleanup rule | More info
Dear Friends
A heat exchanger is being fabricated as per ASME Sec VIII Div.1.
Service Temp is @ 480 degree C.
Tubes material is SA 213 T11 - 1Cr,0.5Mo.
Tube sheet material is SB 409 (Alloy 800)- 33Ni, 42Fe,21Cr UNS No. N08800.
We have selected TIG filler as ER NiCr-3 for the tube to tubesheet joint.
Is the selection of filler metal satisfactory or any better alternative ?
Regards
Prem Nautiyal
cell: 9769316004
PREM S NAUTIYAL
CELL : 9769316004
--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com .
Visit this group at https://groups.google.com/group/materials-welding .
For more options, visit https://groups.google.com/d/optout .
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.
No comments:
Post a Comment