Suggest 2 percent addition of nitrogen to argon for gmaw of duplex SS for G48A, temperature asper ASTM.
On 30 Aug 2017 1:17 p.m., "Aby Jose" <abycscec@gmail.com> wrote:
Dear experts,--Here I am preparing WPS for Duplex material using robotic welding machine. The details are as follows.Material designation - SA 790 UNS S32205Pipe dimension - 4", 6 mm thickWelding process- TIG(Root), MAG(fillup & Cap)After the PQT while doing the pitting corrosion test it got failed. The pitting corrosion test was done as per ASTM G 48.For TIG welding earlier I had used 98% Ar + 2% H2 as shielding gas. Now I have changed it to 98%Ar + 2% N2.For MAG welding pulse method is used. Shielding gas used is 98% Ar + 2% CO2. Purging gas used is 99.997 % Ar.Heat i/p calculated is within the range 0.6 to 1.5. Also the interpass temperature was below 120 degree. What else can be the reason for Pitting corrosion? It came more in the capping. So I am worried about the shielding gas used for MAG. Which other shielding gas can I use for the MAG welding of duplex material??Regards,Aby K JoseQA/QC EngineerQatar+97430847911
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com .
Visit this group at https://groups.google.com/group/materials-welding .
For more options, visit https://groups.google.com/d/optout .
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.
No comments:
Post a Comment