Re: [MW:23197] We are facing minor pore defects in CuNi 90/10

By Materials & Welding

Change argon torch cup size bigger and argon flow you may increase



"Vanchinath S.A." <vanchinaths@gmail.com> yazdı:

You may try argon+1.5%Hydrogen as shielding gas.

On 25 Jul 2015 10:15, "Nazz A" <nazzimmm@gmail.com> wrote:
Sir  I am Muhammad.

we are working here in qatar under Qatar Petroleum.  We have to  complete the fire line systrm through Cu Ni.  We are using Tig welding and ising monel 67 CuNi filler wire. With goving back purging as Argon 99.99 % composition.

But still we arr facing the defects as porocity.  We already covered the area and clean the parent metals and filler wire. Using all of materials like cutting disk wire brush clits and everything is non ferrous.  Our present climate is summer here in Arabian dessert.

But in the Radiography,we cant controle the porocity here. Our all welders are wrll expetienced and well occupied. The poricity is always minor and when we cut out and checking its cant show.

Our acceptable criteria is lower than 0.6 mm.

I hope that you will give the right solution on our problem.

Yours regards...

--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at http://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/193c15ab-9484-4301-a2dc-abbc4438e166%40googlegroups.com.
For more options, visit https://groups.google.com/d/optout.


--
Sent from Kaiten Mail. Please excuse my brevity.

Comments

Post a Comment

Popular posts from this blog

Re: [MW:34105] SA266 GR4N 4 Cycle SPWHT

By Materials & Welding
Hi,  You are correct, Minimum refers to the one cycle for which this part will expose until final work shop PWHT. hence mill test certificate shall include this.  Max. SPWHT, refers to additional cycles of heat treatment that are reserved for future repairs during equipment lifetime.  Again, these simulated no. Of cycles shall be specified in MTC.  The idea is we need to make sure that steel mechanical properties are not compromised upon exposure to multiple repairs (i e 4 cycles in your case).  One could say, if steel is subjected to 4 cycles and is ok, then it should by defacto be good for one cycle, yet, this is wrong assumption cause mechanical problems and microstructure of materials varies accordingly based on no. Of cycles for which material will expose. This is apparent in alloy steel and especially for impact test values as an example.  In your case, this forged CS with properties before PWHT can be understood to be " as forged" condition (i.e. Wit...
Post a Comment
Read more

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

By Materials & Welding
Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change.   Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...
Post a Comment
Read more

Materails FAQs

By Materials & Welding
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...
21 comments
Read more