[MW:23152] 20 Chrome/32 Nickel, Nb- Centrifugally cast tubes

Hello Experts

 Client has encountered what appears to be a corrosive attack in the HAZ of the pipe to tee welds on Metaltek 20/32 Nb material. This area was solution annealed at 2000 F for 6 hours. The corroded/eroded areas were not present prior to solution annealing based on previous inspection.
   The area has been penetrant tested with no relevant indications. It has also been examined by phased array with no evidence of cracking. It appears the base metal has eroded under the weld bead in the area of the HAZ.
 Can you please offer opinions on the cause and corrective actions, if possible?

Thanks and Best Regards,

Ramesh

 

By -

No comments:

Post a Comment

Subscribe to: Post Comments (Atom)

Re: [MW:35289] Welding consumable for S355J2WP material

S355 J2 WP  is a weathering structural steel  It has better atmospheric corrosion resistance. Use E 8018 - W1/W2  Electrodes This is regular...

  • Materails FAQs
    Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? ...
  • RE: [MW:5585] Buttering of weld joints
    Definition of buttering from ASME Section IX, QW/QB-492 Definitions:   Buttering:  the addition of material, by welding, on one or bot...
  • WELD AND WELDING SYMBOLS
    Section I. PRINT READING 3-1. GENERAL a. Drawings . Drawing or sketching is a universal language used to convey all necessary information to...