Sir I am Muhammad.
we are working here in qatar under Qatar Petroleum. We have to complete the fire line systrm through Cu Ni. We are using Tig welding and ising monel 67 CuNi filler wire. With goving back purging as Argon 99.99 % composition.
But still we arr facing the defects as porocity. We already covered the area and clean the parent metals and filler wire. Using all of materials like cutting disk wire brush clits and everything is non ferrous. Our present climate is summer here in Arabian dessert.
But in the Radiography,we cant controle the porocity here. Our all welders are wrll expetienced and well occupied. The poricity is always minor and when we cut out and checking its cant show.
Our acceptable criteria is lower than 0.6 mm.
I hope that you will give the right solution on our problem.
Yours regards...
--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at http://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/193c15ab-9484-4301-a2dc-abbc4438e166%40googlegroups.com.
For more options, visit https://groups.google.com/d/optout.
Subscribe to:
Post Comments (Atom)
Re: [MW:35289] Welding consumable for S355J2WP material
S355 J2 WP is a weathering structural steel It has better atmospheric corrosion resistance. Use E 8018 - W1/W2 Electrodes This is regular...
-
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? ...
-
Definition of buttering from ASME Section IX, QW/QB-492 Definitions: Buttering: the addition of material, by welding, on one or bot...
-
Section I. PRINT READING 3-1. GENERAL a. Drawings . Drawing or sketching is a universal language used to convey all necessary information to...
No comments:
Post a Comment