[MW:17245] Re: WPS with PWHT below the lower transformation temperature

dear all,

I under stand B31.3 so now can i make WPS up to 649ºC without requalification of original WPS .

regards,

mohd.

On Saturday, March 23, 2013 10:20:32 AM UTC+3, mohd wrote:

Dear all,

WPS details as per ASME IX  Design Code :B31.3

1) GTAW + SMAW (3mm+ 24mm)

2) Material API 5L x52 Thk : 26.97

3) PWHT 600 +/-20  Time : 1Hr  20min

4) No impact.

 

Can I Re Write WPS with Temperature  670+/-20 as per As per QW-407.1 a (2) ? ( up to below Lower transformation no need re qualification )

Need expert Opinion.

( QW-407 Postweld Heat Treatment

QW-407.1 A separate procedure qualification is

required for each of the following:

(a) For P-Numbers 1 through 6 and 9 through 15F materials,

the following postweld heat treatment conditions

apply:

(1) no PWHT

(2) PWHT below the lower transformation temperature )

Regards,

mohd.

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
 
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
For more options, visit https://groups.google.com/groups/opt_out.